Failure mode of laser welds in lap‐shear specimens of high strength low alloy (HSLA) steel sheets
Asim, Kamran; Lee, J.; Pan, J.
2012-03
Citation
Asim, K. ; Lee, J. ; Pan, J. (2012). "Failure mode of laser welds in lapâ shear specimens of high strength low alloy (HSLA) steel sheets." Fatigue & Fracture of Engineering Materials & Structures 35(3). <http://hdl.handle.net/2027.42/90305>
Abstract
In this paper, the failure mode of laser welds in lap‐shear specimens of non‐galvanized SAE J2340 300Y high strength low alloy steel sheets under quasi‐static loading conditions is examined based on experimental observations and finite element analyses. Laser welded lap‐shear specimens with reduced cross sections were made. Optical micrographs of the cross sections of the welds in the specimens before and after tests are examined to understand the microstructure and failure mode of the welds. Micro‐hardness tests were also conducted to provide an assessment of the mechanical properties in the base metal, heat‐affected and fusion zones. The micrographs indicate that the weld failure appears to be initiated from the base metal near the boundary of the base metal and the heat‐affected zone at a distance away from the pre‐existing crack tip, and the specimens fail due to the necking/shear of the lower left load carrying sheets. Finite element analyses based on non‐homogenous multi‐zone material models were conducted to model the ductile necking/shear failure and to obtain the J integral solutions for the pre‐existing cracks. The results of the finite element analyses are used to explain the ductile failure initiation sites and the necking/shear of the lower left load carrying sheets. The J integral solutions obtained from the finite element analyses based on the 3‐zone finite element model indicate that the J integral for the pre‐existing cracks at the failure loads are low compared to the fracture toughness and the specimens should fail in a plastic collapse or necking/shear mode. The effects of the sheet thickness on the failure mode were then investigated for laser welds with a fixed ratio of the weld width to the thickness. For the given non‐homogenous material model, the J integral solutions appear to be scaled by the sheet thickness. With consideration of the plastic collapse failure mode and fracture initiation failure mode, a critical thickness can be obtained for the transition of the plastic collapse or necking/shear failure mode to the fracture initiation failure mode. Finally, the failure load is expressed as a function of the sheet thickness according to the governing equations based on the two failure modes. The results demonstrate that the failure mode of welds of thin sheets depends on the sheet thickness, ductility of the base metal and fracture toughness of the heat‐affected zone. Therefore, failure criteria based on either the plastic collapse failure mode or the fracture initiation failure mode should be used cautiously for welds of thin sheets.Publisher
Blackwell Publishing Ltd Wiley Periodicals, Inc.
ISSN
8756-758X 1460-2695
Other DOIs
Types
Article
Metadata
Show full item recordCollections
Remediation of Harmful Language
The University of Michigan Library aims to describe library materials in a way that respects the people and communities who create, use, and are represented in our collections. Report harmful or offensive language in catalog records, finding aids, or elsewhere in our collections anonymously through our metadata feedback form. More information at Remediation of Harmful Language.
Accessibility
If you are unable to use this file in its current format, please select the Contact Us link and we can modify it to make it more accessible to you.